因GRC構件的質量一方面會受到時間的考驗，另一方面還會受到使用環(huán)境的侵蝕，所以GRC構件就必須具備耐久性。
Because the quality of GRC components will be tested by time on the one hand and eroded by the service environment on the other hand, GRC components must have durability.
1、抗?jié)B性：是指壓力水通過其內部的能力。如果抗?jié)B性差，則易使GRC構件中的鋼筋銹蝕，影響構件的使用壽命。影響抗?jié)B性的因素主要有水泥的品種、用量、石子粒徑大小 和級配。水灰比的大小以及GRC構件密實程度。
1. Impermeability: refers to the ability of pressurized water to pass through its interior. If the impermeability is poor, it is easy to rust the reinforcement in GRC members and affect the service life of members. The main factors affecting the impermeability are the variety and dosage of cement, stone particle size and gradation. The water cement ratio and the compactness of GRC components.
2、抗凍性：是GRC構件在飽和水狀態(tài)下遭受冰凍時抵抗冰凍破 壞的能力。這是因為GRC構件內部存在著許多連通的或不連通的孔 隙，這些孔隙成為水分的通道和貯水庫，當GRC構件處于飽和水狀 態(tài)下受到冰凍。內部水分凍結，體積可膨脹8%，導致孔隙脹大并 能產生拉應力。所以經過融化、凍結反復循環(huán)，就可能在拉應力超過GRC構件的抗拉強度時，開始產生徽裂縫并不斷擴展和裂縫連 結。后使GRC構件開裂而破壞。
2. Frost resistance: it refers to the ability of GRC members to resist freezing damage when they are frozen in saturated water. This is because there are many connected or disconnected pores in GRC members, which become water channels and reservoirs. When GRC members are in saturated water state, they are frozen. The internal water is frozen, and the volume can expand by 8%, resulting in pore expansion and tensile stress. Therefore, after repeated cycles of melting and freezing, cracks may begin to occur and continue to expand and connect with cracks when the tensile stress exceeds the tensile strength of GRC members. Finally, GRC members are cracked and damaged.
3、耐蝕性：是指GRC構件在使用環(huán)境中，GRC構件抵抗外界 侵蝕介質腐蝕的能力。如抵抗酸、鹽類化學介質的侵蝕，堿骨料 反應和碳化等。這些介質的侵蝕均可使GRC構件的強度降低，或破壞GRC構件結構體積，影響使用壽命。
3. Corrosion resistance: refers to the ability of GRC components to resist the corrosion of external corrosive media in the service environment. Such as resisting the erosion of acid and salt chemical media, alkali aggregate reaction and carbonization, etc. The erosion of these media can reduce the strength of GRC components, or destroy the structural volume of GRC components and affect the service life.